Optical glass

ABSTRACT

An optical glass suitable for precision press molding has a refractive index (nd) of 1.88 or over and an Abbe number (νd) within a range from 22 to 28, comprises, in mass %,  
                                           SiO 2     15-25%         B 2 O 3     0-5%         La 2 O 3     0-5%         TiO 2      5-15%         ZrO 2      0-10%         Nb 2 O 5     30-50%         WO 3     0-5%         CaO    0-10%         BaO    0-10%         Li 2 O    3-12%         Na 2 O    0-10%         K 2 O    0-10%         Bi 2 O 3      0-15%                                          
 
     and has a glass transition point (Tg) within a range from 500° C. to 580° C. The optical glass preferably has a yield point (At) within a range from 550° C. to 640° C.

BACKGROUND OF THE INVENTION

[0001] This invention relates to an optical glass which has optical constants of a refractive index (nd) of 1.88 or over and an Abbe number (νd) within a range from 22 to 28 and is suitable for precision press molding.

[0002] A typical optical glass having a high refractive index is one which contains a large quantity of lead oxide. Since this type of optical glass is stable because of having high resistance to devitrification and has a low glass transition point (Tg), it has been used for precision press molding. For example, Japanese Patent Application Laid-open Publication No. 1-308843 discloses an optical glass suited for precision press molding which comprises a large quantity of lead oxide.

[0003] Since, however, an environment in which precision press molding is performed is kept in a reducing atmosphere for preventing oxidization of the mold, reduced lead precipitates from the surface of a glass if the glass contains lead oxide and this precipitating lead is deposited on the surface of the mold with the result that difficulty arises in maintaining the precision surface of the mold. Further, lead oxide is detrimental to the environment and hence a lead-free optical glass has been desired for.

[0004] Japanese Patent Application Laid-open Publication No. 52-45612 discloses an optical glass of a SiO₂—Nb₂O₅—RO—R₂O system which is free of lead oxide. The refractive index (nd) of this optical glass, however, is within a range from 1.61 to 1.80.

[0005] Japanese Patent Application Laid-open Publication No. 2000-16830 discloses an optical glass which does not contain lead oxide, has a refractive index (nd) of 1.7 or over and has a yield point of 580° C. or below. In this publication, however, there is no disclosure of a specific example which has a refractive index (nd) of 1.88 or over.

[0006] It is an object of the present invention to eliminate the disadvantages of the prior art optical glasses and provide an optical glass suited for precision press molding which has a high refractive index (nd) of 1.88 or over and an Abbe number (νd) within a range from 22 to 28 and also has a low glass transition point (Tg).

SUMMARY OF THE INVENTION

[0007] Laborious studies and experiments made by the inventors of the present invention for achieving the above described object of the invention have resulted in the finding, which has led to the present invention, that an optical glass having a glass transition point (Tg) within a range from 500° C. to 580° C. and a yield point (At) within a range from 550° C. to 640° C., being free of a substance which is detrimental to the environment, and has an excellent capability for precision press molding can be obtained in an optical glass having optical constants of a refractive index (nd) within a range from 1.88 to 1.95 and an Abbe number within a range from 22 to 28.

[0008] For achieving the object of the invention, there is provided an optical glass having a refractive index (nd) of 1.88 or over and an Abbe number (νd) within a range from 22 to 28, comprising, in mass %, SiO₂ 15-25% B₂O₃ 0-5% La₂O₃ 0-5% TiO₂  5-15% ZrO₂  0-10% Nb₂O₆ 30-50% WO₃ 0-5% CaO  0-10% BaO  0-10% Li₂O  3-12% Na₂O  0-10% K₂O  0-10% Bi₂O₃  0-15%

[0009] and having a glass transition point (Tg) within a range from 500° C. to 580° C.

[0010] In one aspect of the invention, the optical glass has a yield point (At) within a range from 550° C. to 640° C.

[0011] The optical glass according to the invention has a refractive index (nd) of 1.88 or over and an Abbe number (νd) within a range from 22 to 28 and has a low glass transition point (Tg) and therefore is suitable for precision press molding. The optical glass preferably has a yield point within a range from 550° C. to 640° C. The optical glass of the present invention has also excellent resistivity to devitrification and, therefore, is suitable for manufacturing a preform used for precision press molding.

DETAILED DESCRIPTION OF THE INVENTION

[0012] In the optical glass of the present invention, the above described content ranges of the respective ingredients have been selected for reasons stated below. In the following description, the content ranges of the respective ingredients are expressed in mass percent. In the present specification, the phrase “be substantially free of” means that the ingredient is not intentionally added but may be mixed as an allowable amount of impurity.

[0013] The SiO₂ ingredient is an essential ingredient which works as a glass forming ingredient and is effective for improving resistance to devitrification. If the amount of this ingredient is less than 15%, this effect is insufficient whereas if the amount of this ingredient exceeds 25%, the target refractive index (nd) of the present invention cannot be achieved. The amount of this ingredient therefore is limited to the range of 15-25%. A preferable range of this ingredient is 16-24% and a more preferable range thereof is 18-22%.

[0014] The GeO₂ ingredient is effective for improving resistance to devitrification and therefore may be added to the glass. Since, however, this ingredient is an expensive ingredient, a preferable range of this ingredient is 0-5%. A more preferable range of this ingredient is 0-4% and the most preferable range thereof is 0-2%.

[0015] The B₂O₃ ingredient is effective for improving resistance to devitrification and lowering the glass transition point (Tg). If the amount of this ingredient exceeds 5%, resistance to devitrification deteriorates rather than improves. The amount of this ingredient therefore is limited to the range of 0-5%. A preferable range of this ingredient is 0-4% and a more preferable range thereof is 0.5-2%.

[0016] The La₂O₃ ingredient is effective for increasing a refractive index while making the glass to one of a low dispersion characteristic. This ingredient is also effective for improving resistance to devitrification by coexisting with the B₂O₃ ingredient. If, however, the amount of this ingredient exceeds 5%, resistance to devitrification deteriorates rather than improves. The amount of this ingredient therefore is limited to the range of 0-5%. A preferable range of this ingredient is 0-4%.

[0017] The TiO₂ ingredient is an essential ingredient which is very important for increasing the refractive index (nd). If the amount of this ingredient is less than 5%, this effect is not satisfactory whereas if the amount of this ingredient exceeds 15%, resistance to devitrification deteriorates. The amount of this ingredient therefore is limited to the range of 5-15%. A preferable range of this ingredient is 8-14% and a more preferable range thereof is 10-13%.

[0018] The ZrO₂ ingredient is effective for increasing the refractive index (nd) and improving chemical durability of the glass. If the amount of this ingredient exceeds 10%, resistance to devitrification deteriorates. The amount of this ingredient therefore is limited to the range of 0-10%. A preferable range of this ingredient is 0-8% and a more preferable range thereof is 2-8%.

[0019] The Nb₂O₅ ingredient is an essential ingredient which is very important for satisfying the target refractive index of the present invention. If the amount of this ingredient is less than 30%, this effect is not sufficient whereas if the amount of this ingredient exceeds 50%, resistance to devitrification deteriorates. The amount of this ingredient therefore is limited to the range of 30-50%. A preferable range of this ingredient is one which exceeds 30% and is less than 50% and a more preferable range thereof is 32-48%.

[0020] The WO₃ ingredient is effective for increasing the refractive index (nd) and improving resistance to devitrification. If the amount of this ingredient exceeds 5%, resistance to devitrification deteriorates rather than improves. The amount of this ingredient therefore is limited to the range of 0-5%. A preferable range of this ingredient is 0-4% and a more preferable range thereof is 0-3%.

[0021] The CaO ingredient is effective for improving resistance to devitrification and adjusting the optical constants. If the amount of this ingredient exceeds 10%, resistance to devitrification and chemical durability deteriorate. The amount of this ingredient therefore is limited to the range of 0-10%. A preferable range of this ingredient is 0-8% and, more preferably, the glass should be substantially free of this ingredient.

[0022] The BaO ingredient is effective for improving resistance to devitrification and adjusting the optical constants. If the amount of this ingredient exceeds 10%, resistance to devitrification and chemical durability deteriorate The amount of this ingredient therefore is limited to the range of 0-10%. A preferable range of this ingredient is 0-8% and a more preferable range thereof is 1-6%. For improving resistance to devitrification and adjusting the optical constants, a preferable range of total amount of CaO and BaO is 0-12%, a more preferable range of the total amount of these ingredients is 0.5-10% and the most preferable range thereof is 1-8%.

[0023] The Li₂O ingredient is an essential ingredient which is effective for substantially lowering the glass transition point (Tg). If the amount of this ingredient is less than 3%, this effect is insufficient whereas if the amount of this ingredient exceeds 12%, resistance to devitrification deteriorates sharply. The amount of this ingredient therefore is limited to the range of 3-12%. A preferable range of this ingredient is 4-11% and a more preferable range thereof is 5-10%.

[0024] The Na₂O ingredient is effective for improving chemical durability by the mixed alkali effect while lowering the glass transition point (Tg). If the amount of this ingredient exceeds 10%, resistance to devitrification deteriorates. The amount of this ingredient therefore is limited to the range of 0-10%. A preferable range of this ingredient is 0-8% and a more preferable range thereof is 0-6%.

[0025] The K₂O ingredient is effective for improving chemical durability by the mixed alkali effect while lowering the glass transition point (Tg). If the amount of this ingredient exceeds 10%, resistance to devitrification deteriorates. The amount of this ingredient therefore is limited to the range of 0-10%. A preferable range of this ingredient is 0-8% and a more preferable range thereof is 0-6%. A preferable range of the total amount of the Li₂O, Na₂O and K₂O ingredients is 3-32%, a more preferable range thereof is 4-24% and the most preferable range thereof is 6-16%.

[0026] The Bi₂O₃ ingredient is effective for lowering the glass transition point (Tg) while maintaining a high refractive index (nd). If the amount of this ingredient exceeds 15%, resistance to devitrification deteriorates. The amount of this ingredient therefore is limited to the range of 0-15%. A preferable range of this ingredient is 0-12% and, more preferably, the glass should be substantially free of this ingredient.

[0027] The Sb₂O₃ ingredients may be optionally added as a refining agent during melting of the glass materials. Addition of this ingredient up to 1% will suffice.

[0028] The optical glass of the present invention should preferably be free of PbO and F₂ which are not suitable for an optical glass for precision press molding.

EXAMPLES

[0029] Examples of the optical glass of the present invention will be described below. The scope of the present invention however is not limited by these examples.

[0030] The following Tables 1 to 3 show compositions of Examples Nos. 1-13 of the optical glass of the invention as well as refractive index (nd), Abbe number (νd), glass transition point (Tg) and yield point (At) of these examples.

[0031] For manufacturing the optical glasses of Examples Nos. 1-13, conventional raw materials such as oxides, carbonates and nitrates were weighed and mixed at a predetermined ratio to constitute the compositions shown in the tables. These raw materials were put in a platinum crucible, melted at a temperature within a range from 1100° C. to 1300° C. for two to five hours and stirred and homogenized. After lowering the temperature to a proper temperature, the melt was cast into a mold and annealed. As to Examples Nos. 1-13, colorless and transparent glasses were obtained. TABLE 1 Examples 1 2 3 4 5 SiO₂ 20.0 21.0 21.0 24.0 18.0 B₂O₃ 1.5 2.0 2.0 0.0 5.0 La₂O₃ 0.0 3.0 3.0 0.0 4.0 TiO₂ 12.0 12.0 12.0 15.0 10.0 ZrO₂ 6.0 6.0 6.0 8.0 6.0 Nb₂O₅ 40.4 38.9 38.9 34.0 39.9 WO₃ 0.0 2.0 2.0 00 0.0 CaO 4.0 2.0 2.0 1.0 0.0 BaO 4.0 4.0 4.0 6.0 8.0 Li₂O 9.0 9.0 6.0 10.0 9.0 Na₂O 0.0 0.0 0.0 0.0 0.0 K₂O 0.0 0.0 3.0 0.0 0.0 Sb₂O₃ 0.1 0.1 0.1 0.0 0.1 GeO₂ 3.0 0.0 0.0 2.0 0.0 Total 100.0 100.0 100.0 100.0 100.0 nd 1.9011 1.9011 1.8973 1.9091 1.9191 νd 25.2 25.2 24.4 25.9 24.0 Tg 539 540 552 542 521 At 589 589 601 572 572

[0032] TABLE 2 Examples 6 7 8 9 SiO₂ 22.0 21.0 21.0 25.0 B₂O₃ 0.0 4.0 0.5 0.0 La₂O₃ 0.0 3.0 3.0 0.0 TiO₂ 5.0 13.0 14.0 8.0 ZrO₂ 6.0 5.0 6.0 2.0 Nb₂O₅ 48.0 36.0 38.5 50.0 WO₃ 0.0 3.0 4.0 0.0 CaO 6.0 0.0 0.0 0.0 BaO 1.0 4.0 2.0 2.0 Li₂O 9.0 4.0 5.0 5.0 Na₂O 0.0 6.0 0.0 0.0 K₂O 0.0 0.0 6.0 8.0 Sb₂O₃ 0.0 1.0 0.0 0.0 GeO₂ 3.0 0.0 0.0 0.0 Total 100.0 100.0 100.0 100.0 nd 1.9071 1.9069 1.9289 1.8838 νd 27.5 23.8 24.2 26.6 Tg 548 523 564 565 At 596 551 633 592

[0033] TABLE 3 Examples 10 11 12 13 SiO₂ 21.0 21.0 20.0 21.0 B₂O₃ 2.0 2.0 1.9 2.0 La₂O₃ 3.0 3.0 3.0 3.0 TiO₂ 12.0 12.0 12.0 12.0 ZrO₂ 6.0 6.0 6.0 6.0 Nb₂O₅ 38.9 30.4 30.0 38.9 WO₃ 2.0 2.0 2.0 2.0 CaO 0.0 2.0 2.0 0.0 BaO 4.0 4.0 4.0 4.0 Li₂O 4.0 9.0 9.0 9.0 Na₂O 4.0 0.0 0.0 2.0 K₂O 3.0 0.0 0.0 0.0 Sb₂O₃ 0.1 0.1 0.1 0.1 GeO₂ 0.0 0.0 0.0 0.0 Bi₂O₃ 0.0 8.5 10.0 0.0 Total 100.0 100.0 100.0 100.0 nd 1.8875 1.8965 1.9048 1.8905 νd 23.9 25.1 24.8 25.1 Tg 545 519 520 519 At 597 568 570 568

[0034] The glass transition point (Tg) and yield point (At) were obtained from a thermal expansion curve which was obtained by heating a specimen having a length of 50 mm and a diameter of 4 mm by elevating temperature at a constant rate of 4° C. per minute and measuring elongation of the specimen and temperature.

[0035] As described above, the optical glass of the present invention has optical constants of a refractive index (nd) of 1.88 or over and an Abbe number (νd) within a range from 22 to 28 and has a glass transition point (Tg) within a range from 500° C. to 580° C. and, therefore, it is suitable for precision press molding. Since the optical glass has excellent resistance to devitrification, it is suitable for manufacturing a preform for precision press molding of the dropping method.

[0036] The optical glass of the present invention is suitable for use as a lens for optical communication for which demand is rapidly increasing in recent years. The lens for optical communication is a glass lens which has functions such as coupling laser beam emitted from an illuminant such as a semiconductor laser to an optical fiber with high efficiency and, therefore, a micro-optical part which is indispensable for optical communication. For this lens, a ball glass or an asphexical lens is normally used and this lens is required to have a high refractive index. The optical glass of the present invention is suited for precision press molding for producing an aspherical lens. 

What is claimed is:
 1. An optical glass having a refractive index (nd) of 1.88 or over and an Abbe number (νd) within a range from 22 to 28, comprising, in mass %, SiO₂ 15-25% B₂O₃ 0-5% La₂O₃ 0-5% TiO₂  5-15% ZrO₂  0-10% Nb₂O₅ 30-50% WO₃ 0-5% CaO  0-10% BaO  0-10% Li₂O  3-12% Na₂O  0-10% K₂O  0-10% Bi₂O₃  0-15%

and having a glass transition point (Tg) within a range from 500° C. to 580° C.
 2. An optical glass as defined in claim 1 having a yield point (At) within a range from 550° C. to 640° C. 